ASTM A967/A967M-17 July 1, 2017 Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts 1.1 This specification covers several different types of chemical passivation treatments for stainless steel parts. It includes recommendations and precautions for descaling, cleaning, and...

Citric Acid Concentration: 4% ONLY in this phase. Immersion Times: 60, 90, and 120 minutes. Bath Temperatures: 38°C (100°F), 60°C (140°F), and 82°C (180°F) Salt Spray Testing per ASTM B 117. Corrosion Resistance Evaluation every 168 hours up to 504 hours of salt spray testing. Parameters resulting in the best corrosion resistance shall be ...

Specifications: ASTM A967 AMS 2700 QQ-P-35 ASTM 380 ASTM F86 AMS 2700 ISO 16048 Most Company Specifications Types: Precision Medical-Grade Passivation Commercial Passivation A-A-A …

astm-a967, adoption notice: standardization specification for chemical passivation treatments for stainless steel parts (31-mar-1997) [superseding qq-p-35] astm-b26/b26m. astm-b26/b26m, adoption notice: aluminum alloy sand castings (15-may-1992) [superseding qq-a-601f] astm-d1000. 1994

ASTM A967-01 Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts . 1. Scope(범위) * Stainless Steel 의 descaling, cleaning, passivation 에 대한 권고 및 예방책을 제시한다.

ASTM International [astm] PDF Price. $57.00. Add to cart Not a Member? Find out how to get ANSI Member Discount Others Also Bought. ASTM A380/A380M-17. Standard Practice for Cleaning, Descaling, and Passivation of Stainless Steel Parts, Equipment, and Systems ... ASTM A967/A967M-13; Included in Packages.

It includes recommendations and precautions for descaling, cleaning, and passivation of stainless steel parts. It includes several alternative tests, with acceptance criteria, for confirmation of effectiveness of such treatments …

Notes. Claudia's Notes: Changes to the new 2013 Edition of A967/A967M can be found in the following areas: Section 1.5 (changed to combined Metric/US units), Revised Section 4.1 and added Section 4.3, Added Notes 2 and 3 to Sections 6 and 7, Revised Section 13.3, Combined Sections 14 through 19 into a new Section 14, Revised Section 22.1 (Now …

Per ASTM A967 and A380, stainless parts are shown to be properly passivated if they resist corrosion in salt spray for just 2 hours. Stainless steel performs relatively poorly in salt spray because the constant exposure to a harsh environment rapidly erodes the passivation layer and prevents it from reforming.

ASTM A967 Chemical Passivation Treatment for Stainless Steel. This covers several different types of chemical passivation treatment for stainless steel parts. The treatments …

ASTM A967, 2005 Edition, September 1, 2005 - Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts This specification covers several different types of chemical passivation treatments for stainless steel parts. It includes recommendations and precautions for descaling, cleaning, and passivation of stainless …

ASTM A967/A967M-17 (CITRIC ACID) 7.1.1.1 Citric 1—The solution shall contain 4 to 10 weight percent of citric acid. The parts shall be immersed for a minimum of 4 min at a temperature in the range from 60 to 70°C [140 to 160°F] 7.1.1.2 Citric 2—The solution shall contain 4 to 10 weight percent of citric acid.

Full Description. 1.1 This specification covers several different types of chemical passivation treatments for stainless steel parts. It includes recommendations …

1 This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee A01.14 on …

ASTM A 967/A967M : 2017. Current. Add to Watchlist. Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts. Available format (s): Hardcopy, PDF. Language (s): English. Published date: 07-01-2017. Publisher: American Society for Testing and Materials.

ASTM A967/A967M-17. July 1, 2017. Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts. 1.1 This specification covers several …

ASTM A967. General industries use this standard to describe and control the passivation of stainless steel. Passivation is a process of making stainless steel more stainless than it would be if left alone. It is based on using an acid (nitric or citric) under highly controlled conditions to remove free iron particles from the surface and to help form a metal oxide …

ASTM B 117 salt spray testing for 2 to 3 hours, and then evaluated for signs of red rust. Red rust is considered a failure for passivation. In addition, the stainless steel test specimens were also examined for signs of IGA (intergranular attack) and pitting after being treated in the optimized nitric, optimized citric acid, and 3

Standard Guide for Descaling and Cleaning Titanium and Titanium Alloy Surfaces. Buy ASTM A 967 A967M 2017 chemical passivation treatments for stainless …

For example, ASTM A967 contains more options for passivation verification tests while AMS2700 provides more guidance on sampling large batches of components for testing and inspection after passivation. As the most direct linear descendant of QQ-P-35, AMS 2700 naturally shows its "heritage". QQ-P-35 types II, VI, VII and VIII are equivalent ...

Both AMS 2700 and ASTM A967 base their nitric acid passivation methods on using 42° Baume nitric acid. The Baume scale is a measurement of specific gravity. Positive degrees of Baume indicate chemicals or solutions denser than water. 42° Baume nitric acid corresponds to a 1.4 specific gravity solution of nitric acid that is roughly 67% …

1.6 The following precautionary caveat pertains only to the test method portions, Section 14 of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory …

Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts1 This standard is issued under the fixed designation A 967; the number immediately following …

The following spec refers to ASTM A380 for passivation of stainless steel and thus allows the use of ASTM A967: MIL-DTL-14072D/E/F (Table IV. Finish E300) The spec MIL-T-704K in section 3.2.6 directly describes a passivation process analogous to QQ-P-35's type II followed by a chromate post-treatment. However, QQ-P-35 assigns this process as ...

The ASTM A967 passivation standard applies to the cleaning, passivation and testing of stainless steel parts. Chemical passivation removes free iron and other surface contaminants from stainless steel parts, improving corrosion resistance. Stainless steel passivation performed to the ASTM A967 standards meets these standards by passing …

1. Passivation Process: ASTM A967 defines the passivation process as the removal of free iron or other foreign matter from the surface of stainless steel by means of a chemical treatment. This treatment encourages the formation of a passive oxide layer, strengthening the steel's resistance to corrosion. 2.

1.1 This practice covers recommendations and precautions for cleaning, descaling, and passivating of new stainless steel parts, assemblies, equipment, and installed systems. These recommendations are presented as procedures for guidance when it is recognized that for a particular service it is desired to remove surface contaminants that …

Full Description. 1.1 This specification covers several different types of chemical passivation treatments for stainless steel parts. It includes recommendations and precautions for descaling, cleaning, and passivation of stainless steel parts. It includes several alternative tests, with acceptance criteria, for confirmation of effectiveness of ...

ASTM A967 and ASTM A380 have similar mechanical properties. Both materials have a yield strength of 205 MPa and a tensile strength of 520 MPa. The main difference is that ASTM A967 has a higher elongation at break (10%) than ASTM A380 (8%). This means that ASTM A967 is more ductile than ASTM A380 and is better suited …

ASTM-A967, "Standardization Specification for Chemical Passivation Treatments for Stainless Steel Parts", was adopted on 31-MAR-97 for use by the Department of Defense (DoD). Proposed changes by DoD activities must be submitted to the DoD Adopting Activity: Defense Supply Center Richmond, Attn: DSCR-VFT/VEA, Richmond, VA 23297-5610.